Type: | Stainless Steel Sheets |
---|---|
Standard: | ASTM, AISI, GB, JIS, DIN, EN |
Grade: | 300 Series |
Certification: | ISO, IBR, AISI |
Technique: | Cold Rolled |
Surface Treatment: | Polished |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Thickness | Cold rolled: 0.1mm-8mm |
Hot rolled: 3mm-160mm | |
Length | 0.5~10m or customized |
Width | 0.5~3m or customized |
Standard | ASTM, AISI, DIN, EN, GB, JIS |
Grade | Mainly: 201, 202, 304, 304L, 304H, 316, 316L, 316Ti, 2205, 330, 630, 660, 409L, 321, 310S, 410, 416, 410S, 430, 347H, 2Cr13, 3Cr13 etc 300series: 301, 302, 303, 304, 304L, 309, 309S, 310, 310S, 316, 316L, 316Ti, 317L, 321, 347 200series: 201, 202, 202Cu, 204 400series: 409, 409L, 410, 420, 430, 431, 439, 440, 441, 444 Others: 2205, 2507, 2906, 330, 660, 630, 631,17-4ph,17-7ph, S318039 904L,etc Duplex stainless steel: S22053, S25073, S22253, S31803, S32205, S32304 Special Stainless Steel: 904L, 347/347H, 317/317L, 316Ti, 254Mo |
Technique | Cold rolled, Hot rolled |
Surface | 2B, 2D, BA, HL, 4K, 8K, NO.1, NO.3, NO.4 |
Edge | Mill edge/Slit edge |
Certificates | BV, ISO, SGS, CE |
MOQ | 1 ton |
Payment terms | TT(30% deposit advance, 70% balance) or L/T at sight |
Price term: | EX-FACTORY, FOB, CIF or CFR |
Delivery time | 10~20days after receiving deposit |
Productivity | 10000 tons/month |
Application | Escalator, Elevator, Doors Furniture Production tools, Kitchen appliances, freezers, cold rooms Auto Parts Machinery and Packaging Equipment and Medical devices Transport system |
STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
SS 301 | 1.4310 | S30100 | SUS 301 | - | - | - | - |
SS 301L | - | S30103 | SUS 301L | - | - | - | - |
SS 304 | 1.4301 | S30400 | SUS 304 | 304 S31 | 08Х18Н10 | Z7CN18‐09 | X5CrNi18-10 |
SS 304L | 1.4306 / 1.4307 | S30403 | SUS 304L | 304 S11 | 03Х18Н11 | Z3CN18‐10 | X2CrNi18-9 / X2CrNi19-11 |
SS 310 | 1.4841 | S31000 | SUS 310 | 310 S24 | 20Ch25N20S2 | - | X15CrNi25-20 |
SS 310S | 1.4845 | S31008 | SUS 310S | 310 S16 | 20Ch23N18 | - | X8CrNi25-21 |
SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316 S31 / 316 S33 | - | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316 S11 / 316 S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
SS 321 | 1.4541 | S32100 | SUS 321 | - | - | - | X6CrNiTi18-10 |
SS 409 | 1.4512 | S40900 | - | 409 S19 | SUH 409 | Z3CT12 | - |
SS 410 | 1.4006 | S41000 | SUS 410 | 410 S21 | - | Z10C13 / Z13C13 | X12Cr13 |
SS 420 | 1.4021 | S42010 | SUS420J1 | 420 S29 / 420 S37 | - | - | X20Cr13 |
SS 420J1 | 1.4021 | S42010 | SUS420J1 | 420 S29 | - | Z20C13 | X20Cr13 |
SS 420J2 | 1.4028 | S42000 | SUS420J2 | 420S37 | - | Z20C13 | X20Cr13 |
SS 430 | 1.4016 | S43000 | SUS 430 | 430 S17 | - | Z8C17 | X10Cr17 |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
SS 301 | 0.15 max | 2.0 max | 1.0 | 0.045 max | 0.030 max | 16.0 - 18.00 | - | 6.00 - 8.00 | - |
SS 301L | 0.03 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 16.0 - 18.0 | - | 6.00 - 8.00 | - |
SS 304 | 0.08 max | 2.0 max | 0.75 max | 0.045 max | 0.030 max | 18.0 - 20.0 | - | 8.00 - 11.00 | - |
SS 304L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.0 - 20.0 | - | 8.00 - 13.00 | - |
SS 310 | 0.08 max | 2.0 max | 1.50 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
SS 310S | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
SS 316 | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 16.00 - 18.00 | 2.00 - 3.00 | 11.00 - 14.00 | 67.845 min |
SS 316L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 16.00 - 18.00 | 2.00 - 3.00 | 10.00 - 14.00 | 68.89 min |
SS 316Ti | 0.08 max | 2.0 max | 0.75 max | 0.045 max | 0.030 max | 16.00 - 18.00 | 2.00 - 3.00 | 10.00 - 14.00 | 68.395 min |
SS 321 | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 - 19.00 | - | 9.00 - 12.00 | - |
SS 405 | 0.25 max | 2.0 max | 1.50 max | 0.045 max | 0.030 max | 24.00 - 26.00 | - | 19.00 - 22.00 | - |
SS 409 | 0.08 max | 1.0 max | 1.0 max | 0.045 max | 0.045 max | 11.75 max | - | - | - |
SS 410 | 0.15 max | 1.50 max | 1.0 max | 0.04 max | 0.020 max | 11.50 - 13.50 | - | 0.0 - 0.75 | Balance |
SS 420 | 0.16 - 0.25 | 1.50 max | 1.0 max | 0.04 max | 0.015 max | 12.00 - 14.00 | - | - | - |
SS 430 | 0.08 max | 1.0 max | 1.0 max | 0.04 max | 0.02 max | 16.00 - 18.00 | - | - | Balance |
Grade | Density | Melting Point | Tensile Strength ksi (min.) | Yield Strength (0.2%Offset) ksi (min.) | Elongation |
301 1/4 | - | - | 125 | 75 | ≥25% (in 50 mm) |
301 1/2 | - | - | 150 | 110 | 18% |
301 Full Hard | - | - | 185 | 140 | 9% |
SS 301L | - | - | 515 | 205 | 40% |
SS 304/304L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
SS 310/310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
SS 316/316L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
SS 316Ti | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 35% |
SS 321 | 8.0 g/cm3 | 1457 °C (2650 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 35% |
SS 405 | - | - | 515 | 205 | 40% |
SS 409 | - | - | 450 | 240 | 25% |
SS 410 | - | - | 450 - 510 | 205 - 290 | 20% - 34% |
SS 420/420J1/420J2 | - | - | 650 - 950 | 400 - 600 | 10% - 12% |
SS 430 | - | - | 450 - 600 | 260 | 20% |
Surface | Definition | Application |
No.1 | The surface finished by heat treatment and pickling or processes corresponding there to after hot rolling. | Chemical tank, pipe etc. |
2D | When finishing acid cleaning by heat treatment or equivalent processing.Temper cold rolling is performed till proper gloss is acquired. | Areas without surface gloss requirement,such as construction, DDQ and general purpose. |
2B | Those finished, after cold rolling, by heat treatment, pickling or other equivalent treatment and lastly by cold rolling to given appropriate luster.The surface brightness and flatness of No.2B is better than No.2D. No.2B could nearly satisfy comprehensive uses. | Medical equipment, Food industry, Construction material, Kitchen utensils etc. |
No.3 | Polished with abrasive belt of git#100 to #200, have better brightness with discontinuous coarse stria. | Kitchen utensils, Building construction etc. |
No.4 | Polished with abrasive belt of grit #150 to #180,have better brightness with discontinuous coarse stria,but thinner than No.3. | Kitchen utensils, Building construction, Medical equipment etc. |
Hairline | Polished with abrasive belt of grit #150 to #320 on the NO.4 finish and has continuous polishing streaks. | Building Construction etc. |
BA (No.6) | Cold rolled, bright annealed and skin-passed, the product have excellent brightness and good reflexivity. | Kitchen utensils, Electric equipment, Building construction etc. |
Mirror (No.8) | The product have excellent brightness and prefer reflexivity can to be the mirror. | Building construction, decoration etc. |
We can produce different sizes, thicknesses, widths and materials according to your requirements
HR VS CR | ||
HR | CR | |
Processing | The whole process is done at high temperature and at the end is being cooled down | Cold rolled steel is heated and cooled at the room temperature and then rolled after again |
Advantage | - Easier to make: heat it up, push through, cool down and that's it! - Cheaper than cold rolled - Hot rolled steel is allowed to cool at room temperature and it's free from internal stresses that can arise from quenching or work-hardening processes - Most popular shapes are hot-rolled (UC, UB, SHS, RHS, PFC, flats etc.) |
- accurate shape (consistent and straight) - a wider range of surface finishes - a smooth and shinier surface - bars are true and square and have well-defined edges and corners - Tubes have better concentric uniformity and straightness. |
Disadvantage | - dimensional imperfections caused by heating (expanding) and cooling down (shrink, warpage) - rough texture on a surface, need to be removed and buffed before painting - Slight distortions |
- more expensive - fewer shapes available cold-rolled (sheets, box section shapes: CHS, SHS, RHS) - additional treatments can create internal stress within the material; this can cause unpredictable warping if the steel is not stress relieved prior to cutting, grinding, or welding. |
1) Packaging: 3 layers of packing. Inside is craft paper, Middle is water plastic film and outside GI steel sheet to be covered by steel strips with lock, with inner coil sleeve or as customers' requirements.
2) Shipping: We have long-term cooperation with many experienced shipping companies and will find the most suitable mode of transportation for you.
3) Trade terms: FOB/CIF/CFR
4) Shipping port: Qingdao/Tianjin/Shanghai
5) Shipment: A: Length: ≤6m, loaded in 20GP Container. B: Length: ≤12m, loaded in 40GP Container.
Remark: Size of 20GP Container (inside :5898*2352*2393mm); Size of 40GP Container (inside:12032*2352*2393mm); Size of 40HQ Container (inside:12032*2352*2698mm).
6) Delivery time: Normal size: 7-15days send from warehouse directly. Special size:15-30 days custom made for you.